Study of Galvanized Steel Corrosion Resistance in Simulated Seawater

Abstract

The current laboratory experiments investigated the corrosion resistance of galvanized steel in artificial seawater (ASW). After the coupons were immersed in ASW for varying time durations (7 and 14 days) at room temperature, the corrosion rates based on the weight loss were determined. Following exposure to carbon steel for 7 and 14 days, corrosion rates were 0.1193mmpy and 0.1373mmpy, respectively. Methods of Scanning Electron Microscopy (SEM) and Energy Dispersive X-Ray (EDX) Analysis characterized the surface composition of their corrosion product. The visible corrosion product is hematite and lepidocrocite. This result allows us to understand the corrosion behavior of galvanized steel used in the marine environment.

Country : Indonesia

1 Yustina M Pusparizkita2 Vivi A Fardillah3 J Jamari4 A P Bayuseno

  1. Department of Environmental Engineering, Faculty of Engineering, Diponegoro University, Jl. Prof Soedarto SH, Semarang, 50275, Central Java, Indonesia
  2. Department of Mechanical Engineering, Faculty of Engineering, Diponegoro University, Jl. Prof Soedarto SH, Semarang, 50275, Central Java, Indonesia
  3. Department of Mechanical Engineering, Faculty of Engineering, Diponegoro University, Jl. Prof Soedarto SH, Semarang, 50275, Central Java, Indonesia
  4. Department of Mechanical Engineering, Faculty of Engineering, Diponegoro University, Jl. Prof Soedarto SH, Semarang, 50275, Central Java, Indonesia

IRJIET, Volume 7, Issue 5, May 2023 pp. 262-267

doi.org/10.47001/IRJIET/2023.705034

Full Paper
Download

References

  1. F. Delaunois, F. Tosar, and V. Vitry, “Corrosion behaviour and biocorrosion of galvanized steel water distribution systems,” Bioelectrochemistry, vol. 97, pp. 110–119, Jun. 2014, doi: 10.1016/j.bioelechem.2014.01.003.
  2. A.P. Yadav, H. Katayama, K. Noda, H. Masuda, A. Nishikata, and T. Tsuru, “Effect of Fe–Zn alloy layer on the corrosion resistance of galvanized steel in chloride containing environments,” Corrosion Science, vol. 49, no. 9, pp. 3716–3731, Sep. 2007, doi: 10.1016/j.corsci.2007.03.039.
  3. S. Rossi, M. Pinamonti, and M. Calovi, “Influence of soil chemical characteristics on corrosion behaviour of galvanized steel,” Case Studies in Construction Materials, vol. 17, p. e01257, Dec. 2022, doi: 10.1016/j.cscm.2022.e01257.
  4. A.Shokri and M. Sanavi Fard, “Corrosion in seawater desalination industry: A critical analysis of impacts and mitigation strategies,” Chemosphere, vol. 307, p. 135640, Nov. 2022, doi: 10.1016/j.chemosphere.2022.135640.
  5. G. A. El-Mahdy, A. Nishikata, and T. Tsuru, “Electrochemical corrosion monitoring of galvanized steel under cyclic wet–dry conditions,” Corrosion Science, vol. 42, no. 1, pp. 183–194, Jan. 2000, doi: 10.1016/S0010-938X(99)00057-8.
  6. A.P. Yadav, A. Nishikata, and T. Tsuru, “Degradation mechanism of galvanized steel in wet–dry cyclic environment containing chloride ions,” Corrosion Science, vol. 46, no. 2, pp. 361–376, Feb. 2004, doi: 10.1016/S0010-938X(03)00153-7.
  7. X. Hou, L. Gao, Z. Cui, and J. Yin, “Corrosion and Protection of Metal in the Seawater Desalination,” IOP Conference Series: Earth and Environmental Science, vol. 108, no. 2, p. 022037, Jan. 2018, doi: 10.1088/1755-1315/108/2/022037.
  8. E.-S. M. Sherif, “Comparative Study on the Inhibition of Iron Corrosion in Aerated Stagnant 3.5 wt % Sodium Chloride Solutions by 5-Phenyl-1H-tetrazole and 3-Amino-1,2,4-triazole,” Ind. Eng. Chem. Res., vol. 52, no. 41, pp. 14507–14513, Oct. 2013, doi: 10.1021/ie400725z.
  9. Y. Song, G. Jiang, Y. Chen, P. Zhao, and Y. Tian, “Effects of chloride ions on corrosion of ductile iron and carbon steel in soil environments,” Scientific Reports, vol. 7, no. 1, p. 6865, Jul. 2017, doi: 10.1038/s41598-017-07245-1.
  10. L. Feng et al., “A parametric study on effects of pitting corrosion on steel plate’s ultimate strength,” Applied Ocean Research, vol. 95, p. 102026, Feb. 2020, doi: 10.1016/j.apor.2019.102026.
  11. J.-H. Ahn, W. R. Choi, S. H. Jeon, S.-H. Kim, and I.-T. Kim, “Residual compressive strength of inclined steel tubular members with local corrosion,” Applied Ocean Research, vol. 59, pp. 498–509, Sep. 2016, doi: 10.1016/j.apor.2016.07.002.
  12. M. Lv, M. Du, X. Li, Y. Yue, and X. Chen, “Mechanism of microbiologically influenced corrosion of X65 steel in seawater containing sulfate-reducing bacteria and iron-oxidizing bacteria,” Journal of Materials Research and Technology, vol. 8, no. 5, pp. 4066–4078, Sep. 2019, doi: 10.1016/j.jmrt.2019.07.016.
  13. L. Peng, M. G. Stewart, and R. E. Melchers, “Corrosion and capacity prediction of marine steel infrastructure under a changing environment,” Structure and Infrastructure Engineering, vol. 13, no. 8, pp. 988–1001, Aug. 2017, doi: 10.1080/15732479.2016.1229798.
  14. Y. Cai et al., “Quantitative Understanding of the Environmental Effect on B10 Copper Alloy Corrosion in Seawater,” Metals, vol. 11, no. 7, 2021, doi: 10.3390/met11071080.
  15. K. Godbole and K. Mondal, “Effect of Salinity, Total Dissolved Solids, Conductivity, and pH on Corrosion Behavior of Different Microstructures Made from High-Carbon Rail Steel,” Journal of Materials Engineering and Performance, vol. 31, no. 7, pp. 5630–5640, Jul. 2022, doi: 10.1007/s11665-022-06630-w.
  16. R. Javaherdashti, “Microbiologically Influenced Corrosion (MIC),” in Microbiologically Influenced Corrosion: An Engineering Insight, R. Javaherdashti, Ed., Cham: Springer International Publishing, 2017, pp. 29–79. doi: 10.1007/978-3-319-44306-5_4.
  17. B. Tansel and K. Zhang, “Effects of saltwater intrusion and sea level rise on aging and corrosion rates of iron pipes in water distribution and wastewater collection systems in coastal areas,” Journal of Environmental Management, vol. 315, p. 115153, Aug. 2022, doi: 10.1016/j.jenvman.2022.115153.
  18. S. Lyon, “1 - Overview of corrosion engineering, science and technology,” in Nuclear Corrosion Science and Engineering, D. Féron, Ed., Woodhead Publishing, 2012, pp. 3–30. doi: 10.1533/9780857095343.1.3.
  19. S. Chen and D. Zhang, “Corrosion behavior of Q235 carbon steel in air-saturated seawater containing Thalassospira sp.,” Corrosion Science, vol. 148, pp. 71–82, Mar. 2019, doi: 10.1016/j.corsci.2018.11.031.
  20. J. Kvarekvål and J. Moloney, “6 - Sour corrosion,” in Trends in Oil and Gas Corrosion Research and Technologies, A. M. El-Sherik, Ed., Boston: Woodhead Publishing, 2017, pp. 113–147. doi: 10.1016/B978-0-08-101105-8.00006-1.
  21. X. Wang and R. E. Melchers, “Corrosion of carbon steel in presence of mixed deposits under stagnant seawater conditions,” Journal of Loss Prevention in the Process Industries, vol. 45, pp. 29–42, Jan. 2017, doi: 10.1016/j.jlp.2016.11.013.
  22. D. de la Fuente, J. Alcántara, B. Chico, I. Díaz, J. A. Jiménez, and M. Morcillo, “Characterisation of rust surfaces formed on mild steel exposed to marine atmospheres using XRD and SEM/Micro-Raman techniques,” Corrosion Science, vol. 110, pp. 253–264, Sep. 2016, doi: 10.1016/j.corsci.2016.04.034.
  23. F. Tian, X. He, X. Bai, and C. Yuan, “Electrochemical corrosion behaviors and mechanism of carbon steel in the presence of acid-producing bacterium Citrobacter farmeri in artificial seawater,” International Biodeterioration & Biodegradation, vol. 147, p. 104872, Feb. 2020, doi: 10.1016/j.ibiod.2019.104872.
  24. M. Mohammadikish, “Hydrothermal synthesis, characterization and optical properties of ellipsoid shape α-Fe2O3 nanocrystals,” Ceramics International, vol. 40, no. 1, Part B, pp. 1351–1358, Jan. 2014, doi: 10.1016/j.ceramint.2013.07.016.

Copyright @ 2026-2017 IRJIET. All Right Reserved.

Developed by Byzero Technologies